MVK 19

HIGH TEMP · LIGHT WEIGHT · EXTENDED LIFE

MAXIMUM ENDURANCE

Designed for long-term operation at temperatures up to 700°F (371°C), MVK-19 was developed to operate in severe environments.  MVK-19 components have been qualified in the hottest compressor stages of military and commercial jet engines for over 20 years. 

Reinforced with continuous fiber, MVK-19 components exhibit excellent thermal and mechanical stability under extreme conditions.  MVK-19 components are available exclusively from Maverick Molding Company.

Download Product Data Sheet

For MSDS information please fill out our contact form.

Key Properties

Glass Transition Temperature:700°F - 725°F (371°C - 385°C)
Thermal Oxidative Stability:2 - 4% weight loss in simulated jet engine environment at 700ºF (371°C), 70 psi, 100 hours
Thermal Gravimetric Analysis:0.05% weight loss from 392°F - 617°F (200°C - 325ºC)

Typical Properties

Mechanical PropertiesTemperatureTest MethodUnitsTypical Values
Tensile StrengthRTASTM D3039Ksi17.0
Tensile ModulusRTASTM D3039Msi2.1
Tensile Elongation @ BreakRTASTM D3039%3.0
Tensile Strength500°F (260°C)ASTM D3039Ksi-
Tensile Modulus500°F (260°C)ASTM D3039Msi-
Tensile Elongation @ Break500°F (260°C)ASTM D3039%-
Compressive StrengthRTASTM D695Ksi35.1
Compressive ModulusRTASTM D695Msi0.75
Compressive Strength500°F (260°C)ASTM D695Ksi-
Compressive Modulus500°F (260°C)ASTM D695Msi-
Shear StrengthRTASTM D5379Ksi11.0
Shear ModulusRTASTM D5379Msi-
Flexural StrengthRTASTM D790Ksi27.5
Flexural ModulusRTASTM D790Msi3.0
Flexural Strength500°F (260°C)ASTM D790Ksi17.0
Flexural Modulus500°F (260°C)ASTM D790Msi1.45
Physical PropertiesTemperatureTest MethodUnitsTypical Values
 DensityRTASTM D792(gm/cm^3)1.65
 Poisson's RatioRTASTM D3039-0.28
 Hardness, Rockwell "E"RTASTM D785-50
Dry TgRT - 750°FASTM E1640°F (°C)725 (385)
Wet Tg °FRT - 750°FASTM E1640°F (°C)-
Moisture AbsorptionRT---
CTE Parallel to Molding DirectionRT to 450°FASTM E831In-inE-6/°F1.5
CTE Transverse to Molding DirectionRT to 450°FASTM E831In-inE-6/°F8.0
TOS Wt. Loss (100 hrs, 70 psi)700°F (371°C)E50TF534% wt. loss2.5
TOS Wt. Loss (120 hrs, 150 psi)600°F (316°C)E50TF534% wt. loss-
Wear PropertiesTemperatureTest MethodUnitsTypical Values
Coefficient of FrictionRT to 700°FASTM G99-0.19
Wear @ 30N Load/500 rpm/2 hrs400°F (205°C)ASTM G99µm-
Wear @ 30N Load/500 rpm/2 hrs500°F (260°C)ASTM G99µm-
Thermal ConductivityRTASTM E1225-04BTU/Hrs.ft°F-
Thermal Conductivity662°F (350°C)ASTM E1225-05BTU/Hrs.ft°F-
Specific Heat CapacityRTASTM E1269-05W/mK-
Specific Heat Capacity662°F (350°C)ASTM E1269-06J/kg°C-

Disclaimer: The data listed herein fall within the normal range of properties but should not be used to establish specification limits or used alone as the basis of design. Maverick Molding assumes no obligations or liabilities for any advice furnished or for any results obtained with respect to this information. All such advice is given and accepted at buyer’s risk.